基于聚多巴胺的超疏水棉织物的一锅法制备及其油水分离性能
张红亮, 赵国庆, 欧军飞, Amirfazli Alidad

Superhydrophobic Cotton Fabric Based on Polydopamine via Simple One-Pot Immersion for Oil Water Separation
ZHANG Hongliang, ZHAO Guoqing, OU Junfei, Amirfazli Alidad
表4 TF-3C-5C超疏水织物的耐用性与文献值的对比
Table 4 Wettability variation for the TF-3C-5C sample and control samples in references
SF-3C-5CComparisonSamples in referenceRef.
Ultrasonic cleaningCA=157.2° and SA=9° after 1 h in ethanol>CA varied from 159° to 150° after 1 h in ethanol[22]
<CA varied from 154° to 152° after 24 h in acetone[23]
LaunderingCA=152° and SA=18° after 25 cycles>CA varied from 157° to 147° after 20 cycles[20]
<CA varied from 152° to ca. 150° after 100 cycles[24]
Water BoilingCA=152.2° and SA=18° after 48 h>CA varied to ca. 150° and SA increased to 15° after 35 min[25]
Alkali SoakingCA=153.2° and SA=14° after 48 h>CA varied from 156.3° to 152.2° after 48 h[20]
CA varied from 156.9° to 151.6° after 48 h[26]
Acid SoakingCA>157.7° and SA=6° after 48 h>

CA varied from 154.7° to 150.6° after 12 h

CA varied from 156.9° to 142.3° after 24 h

CA varied from 156.3° to 152.5° after 48 h

[27]

[26]

[20]

AbradingCA=132.6° and SA<30° after 200 cycles<CA and SA remained almost unchanged after 200 cycles[28]