Ru对一种高W镍基单晶合金蠕变性能的影响 |
梁爽, 刘智鑫, 刘丽荣, 梁金广, 纪良博, 邵华阳 |
Effect of Ru on Creep Properties of a High Tungsten Containing Ni-based Single Crystal Superalloy |
LIANG Shuang, LIU Zhixin, LIU Lirong, LIANG Jinguang, JI Liangbo, SHAO Huayang |
图8 合金3经1070℃/137 MPa蠕变50 h、200 h和蠕变断后的组织形貌 |
Fig.8 Microstructure of alloy 3 after creep at 1070℃/137 MPa for 50 hours (a), 200 hours (b) and creep fracture (c) |