C和W对低合金Cr-Mo钢焊缝金属组织和冲击韧性的影响

朱高文, 吴栋, 陆善平

Effect of C- and W-content on Microstructure and Toughness of Weld Metal for Low Alloy Cr-Mo Steel

ZHU Gaowen, WU Dong, LU Shanping

表2 熔敷金属和母材的化学成分

Table 2 Chemical compositions of deposited metal and base metal (mass fraction, %)

Elements C W Cr Mo Si Mn Fe 02C 0.021 0.04 2.03 0.62 0.29 0.57 Bal. 05C/04W 0.042 0.038 2.02 0.62 0.24 0.49 Bal. 08C 0.075 0.04 2.05 0.63 0.25 0.49 Bal. 0W 0.058 0 2.04 0.63 0.23 0.51 Bal. 09W 0.054 0.086 1.97 0.64 0.24 0.43 Bal. Base metal 0.13 <0.05 2.17 0.95 0.24 0.46 Bal.