18.5%Cr高Mn型节镍双相不锈钢大变形热压缩的组织和再结晶行为
Microstructure and Recrystallization Behavior of 18.5%Cr High-Mn Low-Ni Type Duplex Stainless Steel during Hot Compression with Large Deformation
18.5%Cr高Mn型节镍双相不锈钢大变形热压缩的组织和再结晶行为 |
| 潘晓宇, 杨银辉, 倪珂, 曹建春, 钱昊 |
|
Microstructure and Recrystallization Behavior of 18.5%Cr High-Mn Low-Ni Type Duplex Stainless Steel during Hot Compression with Large Deformation |
| PAN Xiaoyu, YANG Yinhui, NI Ke, CAO Jianchun, QIAN Hao |
| 图5 在应变速率为0.1 s-1、不同变形温度条件下试样的TEM照片和电子衍射花样 |
| Fig.5 TEM images of specimens deformed at strain rate of 0.1 s-1 and different deformation temperatures (a, b, c) 1123 K; (d, e, f) 1223 K; (g, h, i) 1323 K |
|
|