C和B的含量对K417G镍基高温合金的凝固行为和高温持久性能的影响
Influence of C- and B-content on Solidification and High Temperature Stress Rupture Behavior of Nickel-based Superalloy K417G
C和B的含量对K417G镍基高温合金的凝固行为和高温持久性能的影响 |
| 舒德龙, 严志, 王道红, 谢君, 侯桂臣, 盛乃成, 李金国, 于金江, 孙晓峰, 周亦胄 |
|
Influence of C- and B-content on Solidification and High Temperature Stress Rupture Behavior of Nickel-based Superalloy K417G |
| SHU Delong, YAN Zhi, WANG Daohong, XIE Jun, HOU Guichen, Naicheng SHENG, LI Jinguo, YU Jinjiang, SUN Xiaofeng, ZHOU Yizhou |
| 图8 不同C、B含量K417G合金在950℃/235 MPa条件下的持久寿命 |
| Fig.8 Stress rupture life of the K417G alloys with different C and B contents under the condition of 950℃/235 MPa |
|
|