形变和退火对Fe47Mn30Co10Cr10B3间隙高熵合金微观组织结构演变的影响
陈扬1, 涂坚1,2(
), 张琰斌1, 谭力1, 尹瑞森3, 周志明1,2
), 张琰斌1, 谭力1, 尹瑞森3, 周志明1,2
Effect of Deformation and Annealing Process on Microstructural Evolution of Fe47Mn30Co10Cr10B3 High Entropy Alloy
CHEN Yang1, TU Jian1,2(), ZHANG Yanbin1, TAN Li1, YIN Ruisen3, ZHOU Zhiming1,2
), ZHANG Yanbin1, TAN Li1, YIN Ruisen3, ZHOU Zhiming1,2
图4. 形变温度为液氮低温、室温(26℃)或高温(800℃)形变量为10%时均匀态样品的EBSD图
Fig.4. EBSD maps of homogenized samples with 10% deformation degree under different deformation temperatures: (a1~a4) cryogenic temperature; (b1~b4) room temperature (26℃); (c1~c4) high temperature (800℃)