淬火温度对含铜5Cr15MoV马氏体不锈钢性能的影响

郝欣欣, 席通, 张宏镇, 杨春光, 杨柯

Effect of Quenching Temperature on Microstructure and Properties of Cu-bearing 5Cr15MoV Martensitic Stainless Steel

HAO Xinxin, XI Tong, ZHANG Hongzhen, YANG Chunguang, YANG Ke

图3 5Cr15MoV-4.13Cu在1000℃、1025℃、1050℃、1075℃、1100℃淬火后和5Cr15MoV在1050℃淬火后的SEM照片

Fig.3 SEM images of 5Cr15MoV-4.13Cu quenched at 1000℃ (a), 1025℃ (b), 1050℃ (c), 1075℃ (d), 1100℃ (e) and 5Cr15MoV quenched at 1050℃ (f)