疏水可拉伸碳纳米管/聚二甲基硅氧烷复合薄膜的性能

杨亚威, 常书龙, 上媛媛

Performance of Hydrophobic Stretchable Carbon Nanotubes/Polydimethylsiloxane Composite Films

YANG Yawei, CHANG Shulong, SHANG Yuanyuan

图4 应变为10%、20%、50%、80%、100%条件下MWNTs/PDMS复合薄膜电阻的变化，应变为50%、拉伸速度分别为20 mm/min、40 mm/min、60 mm/min、80 mm/min和100 mm/min条件下MWNTs/PDMS复合薄膜电阻的变化以及MWNTs/PDMS复合薄膜应变为50%循环200圈电阻的变化

Fig.4 Resistance changes of MWNTs/PDMS composite films at strain of 10%, 20%, 50%, 80% and 100% (a), resistance changes of MWNTs/PDMS composite films at strain of 50% at tensile speed of 200%/min, 400%/min, 600%/min, 800%/min and 1000%/min (b) and resistance change of MWNTs/PDMS composite film for 200 cycles at strain of 50% (c)