基于α''组织设计适于激光立体成形的新型高塑性Ti-4.13Al-9.36V合金 |
|||||||||||||||||
| 刘田雨, 朱智浩, 张爽, 董闯, 闵小华, 王清 | |||||||||||||||||
|
A Novel Ti-4.13Al-9.36V Alloy of High Ductility Designed on Base of α''-Microstructure for Laser Solid Forming |
|||||||||||||||||
| LIU Tianyu, ZHU Zhihao, ZHANG Shuang, DONG Chuang, MIN Xiaohua, WANG Qing | |||||||||||||||||
| 表2 Ti-6.05Al-9.36V和Ti-4.13Al-9.36合金α板条宽度随固溶温度的变化 |
|||||||||||||||||
| Table 2 Changes of α laths width in Ti-6.05Al-3.94V and Ti-4.13Al-9.36V with different solution temperature |
|||||||||||||||||
|
|||||||||||||||||