多介质在碳钢腐蚀过程中的协同作用

张少华, 李彦睿, 卫英慧, 刘宝胜, 侯利锋, 杜华云, 刘笑达

Synergistic Effect of Multi-media on Carbon Steel Corrosion

ZHANG Shaohua, LI Yanrui, WEI Yinghui, LIU Baosheng, HOU Lifeng, DU Huayun, LIU Xiaoda

表4 碳钢在CO2(1 bar)+0.1 mol/L Cl-+0/0.05/0.1/0.5 mol/L HCO3-溶液体系中的电化学阻抗谱拟合参数

Table 4 Parameters of Electrochemical Impedance Spectroscopy component values of carbon steel in solutions containing CO2 (1 bar)+0.1 mol/L Cl-+0/0.05/0.1/0.5 mol/L HCO3-

Components 0 mol·L-1 0.05 mol·L-1 0.1 mol·L-1 0.5 mol·L-1 Rs/Ω·cm2 14.77 12.75 7.715 5.83 CPEdl/10-4 F·cm-2 3.53 3.729 4.972 4.401 ndl 0.8442 0.7902 0.7472 0.7542 Rct/Ω·cm2 136.2 196.3 280.9 373.4