热处理对Al-Mg-Ga-In-Sn合金微观结构和铝水反应的影响
|
|
杜邦登, 刘军, 王晓婉, 汪伟, 陈德敏
|
Effect of Heat Treatment on Microstructure and Al-water Reactivity of Al-Mg-Ga-In-Sn Alloys
|
|
DU Bangdeng, LIU Jun, WANG Xiaowan, WANG Wei, CHEN Demin
|
|
表1 热处理态Al?Mg?Ga?In?Sn合金铝晶粒和晶界相的成分
|
Table 1 Compositions of Al grains and grain boundary phases of heat treated Al-Mg-Ga-In-Sn alloys
|
|
Sample /mass fraction | Spectrum | Phase | Element/atom fraction, % |
|---|
| Mg | Al | Ga | In | Sn |
|---|
| 2 %, solution | G | 1 | 1.89 | 96.53 | 1.58 | - | - | | GB | 2 | 66.34 | 2.20 | 1.11 | - | 30.34 | | GB | 3 | 14.30 | 69.94 | 14.36 | 1.40 | - | | GB | 4 | 29.92 | 35.41 | 5.29 | 29.39 | - | | GB | 5 | 34.09 | 26.56 | 19.00 | 20.34 | - | | 3%, solution | G | 6 | 3.09 | 95.52 | 1.39 | - | - | | GB | 7 | 62.40 | 7.19 | - | - | 30.41 | | GB | 8 | 41.69 | 18.06 | 8.01 | 32.24 | - | | GB | 9 | 35.06 | 35.02 | 28.40 | 1.51 | - | | GB | 10 | 38.39 | 27.33 | 22.80 | 11.48 | - | | 4%, solution | G | 11 | 4.22 | 94.71 | 1.07 | - | - | | GB | 12 | 66.29 | 1.05 | 1.08 | - | 31.58 | | GB | 13 | 19.59 | 54.41 | 20.45 | 5.55 | - | | GB | 14 | 33.53 | 27.02 | 20.08 | 19.37 | - | | 5%, solution | G | 15 | 5.10 | 93.95 | 0.95 | - | - | | GB | 16 | 49.86 | 27.85 | - | - | 22.29 | | GB | 17 | 58.57 | 7.59 | 20.33 | 13.52 | - | | GB | 18 | 38.70 | 21.77 | 19.74 | 19.78 | - | | GB | 19 | 27.99 | 49.57 | 22.44 | - | - | | GB | 20 | 36.86 | 23.75 | 6.73 | 32.66 | - | | 3%, aging | G | 21 | 3.11 | 95.50 | 1.39 | - | - | | GB | 22 | 44.33 | 32.34 | 0.95 | - | 22.39 | | GB | 23 | 25.94 | 49.42 | 18.72 | 5.93 | - | | GB | 24 | 25.22 | 47.41 | 2.86 | 24.52 | - | | GB | 25 | 36.24 | 21.29 | 28.27 | 14.20 | - | | 4%, aging | G | 26 | 4.22 | 94.62 | 1.16 | - | - | | GB | 27 | 41.52 | 30.78 | 0.98 | - | 26.72 | | GB | 28 | 35.06 | 35.02 | 28.40 | 1.51 | - | | GB | 29 | 27.57 | 44.67 | 10.83 | 16.93 | - | | GB | 30 | 35.32 | 26.54 | 20.57 | 17.58 | - |
|
|
|