Effect of Heat Treatment on Microstructure and Al-water Reactivity of Al-Mg-Ga-In-Sn Alloys
DU Bangdeng1, LIU Jun2, WANG Xiaowan1, WANG Wei1(), CHEN Demin1()
), CHEN Demin1()
图9. Al-Mg-Ga-In-Sn合金与70℃水接触不同时间后的腐蚀形貌
Fig.9. Corrosion morphologies of Al-Mg-Ga-In-Sn alloys after immersion in water of 70℃ for different time: aged alloy with Mg content of 2% (a) polished; (b) 60 s; (c) enlarged image of (b); (d) 10 min; solution treated alloy with Mg content of 2% (e) 60 s; aged alloy with Mg content of 5% (f) 60 s