两次淬火对HSLA钢组织和冲击韧性的影响
陈刚1,2, 罗小兵1(
), 柴锋1, 杨才福1, 张正延1, 杨志刚2
), 柴锋1, 杨才福1, 张正延1, 杨志刚2
Effect of Double Quenching on Microstructure and Impact Toughness of a High Strength Low Alloy Steel
CHEN Gang1,2, LUO Xiaobing1(), CHAI Feng1, YANG Caifu1, ZHANG Zhengyan1, YANG Zhigang2
), CHAI Feng1, YANG Caifu1, ZHANG Zhengyan1, YANG Zhigang2
图9. DQT工艺实验钢的二次裂纹和主要裂纹扩展形貌
Fig.9. SEM images of (a) secondary crack propagation and (b) main crack propagation for impact specimens treated by DQT process