两次淬火对HSLA钢组织和冲击韧性的影响
陈刚1,2, 罗小兵1(
), 柴锋1, 杨才福1, 张正延1, 杨志刚2
), 柴锋1, 杨才福1, 张正延1, 杨志刚2
Effect of Double Quenching on Microstructure and Impact Toughness of a High Strength Low Alloy Steel
CHEN Gang1,2, LUO Xiaobing1(), CHAI Feng1, YANG Caifu1, ZHANG Zhengyan1, YANG Zhigang2
), CHAI Feng1, YANG Caifu1, ZHANG Zhengyan1, YANG Zhigang2
图2. 两热处理工艺实验钢的冲击功和断面纤维率随温度的变化
Fig.2. Impact energy and percentage of ductile fracture surface-temperature curves for the specimens treated by DQT and CQT