高熵合金FeCoNiTi的微观组织演变和强韧化行为
刘怡1, 徐康1, 涂坚1,2(
), 黄灿1, 吴玮1, 谭力1, 张琰斌1, 尹瑞森3, 周志明1,2
), 黄灿1, 吴玮1, 谭力1, 张琰斌1, 尹瑞森3, 周志明1,2
Microstructure Evolution and Strength-ductility Behavior of FeCoNiTi High-entropy Alloy
LIU Yi1, XU Kang1, TU Jian1,2(), HUANG Can1, WU Wei1, TAN Li1, ZHANG Yanbin1, YIN Ruisen3, ZHOU Zhiming1,2
), HUANG Can1, WU Wei1, TAN Li1, ZHANG Yanbin1, YIN Ruisen3, ZHOU Zhiming1,2
图7. 形变FeCoNiTi高熵合金的不同放大倍数SEM照片
Fig.7. SEM images under the different magnification for the as-deformed FeCoNiTi HEA; two typical types of deformation microstructure are detectable in (a) and (b); the distorted lamellar structure in (c); the lenticular twins in (d)