高熵合金FeCoNiTi的微观组织演变和强韧化行为
|
刘怡 1, 徐康 1, 涂坚 1,2( ), 黄灿 1, 吴玮 1, 谭力 1, 张琰斌 1, 尹瑞森 3, 周志明 1,2
|
Microstructure Evolution and Strength-ductility Behavior of FeCoNiTi High-entropy Alloy
|
LIU Yi 1, XU Kang 1, TU Jian 1,2( ), HUANG Can 1, WU Wei 1, TAN Li 1, ZHANG Yanbin 1, YIN Ruisen 3, ZHOU Zhiming 1,2
|
|
图3. 均匀态FeCoNiTi高熵合金的背散射衍射图
|
Fig.3. Back-scattered electron images of the as-homogenized FeCoNiTi HEA (a) lamellar structure and Widmanstätten laths; (b) Widmanstätten laths showing misorientation of 29.3°, 62.8° and 89.1° (marked by arrows) with respect to the embedding lamellar structure, Widmanstätten laths with three different angles of intersection are revealed, i.e., 39.1°,55.8° and 70.1° (marked by arrows); two Widmanstätten laths showing two shapes: strip in (c) and triangle in (d)
|
|
|
|
|