Preparation and Condensation Behavior of Wear Resistant Al-based Superhydrophobic Materials
WANG Fang1, ZHOU Baoyu1, FENG Wei1,2(), LEI Jialiu1,2, JIANG Yufeng1, WANG Qidi1,3
), LEI Jialiu1,2, JIANG Yufeng1, WANG Qidi1,3
图3. 样品摩擦前和2000次摩擦后表面形貌的对比
Fig.3. Comparison of surface morphology of samples before and after 2000 rubbing test: sample A (no seed layer, hydrothermal reaction 3 h) before (A) and after rubbing (A'); sample B (3 layers of seed layer, hydrothermal reaction 1 h) before (B) and after rubbing (B'); sample C (3 layers of seed layer, hydrothermal reaction 3 h) before (C) and after rubbing (C')