Ti65合金的初级蠕变和稳态蠕变
岳颗1,2,刘建荣1(
),杨锐1,王清江1
),杨锐1,王清江1
Primary Creep and Steady-State Creep of Ti65 Alloy
YUE Ke1,2,LIU Jianrong1(),YANG Rui1,WANG Qingjiang1
),YANG Rui1,WANG Qingjiang1
图7. 蠕变后组织形貌的TEM明场像
Fig.7. TEM images of crept samples at (a) 600℃/160 MPa, (b) 650℃/160 MPa. The residual β phase in colonies partially dissolved and the silicides coarsened significantly after creep deformation