Cu含量和烧结温度对Fe-Cu基粉末冶金复合材料摩擦磨损性能的影响
石磊1,赵齐1(
),罗成1,陈浩1,杨继彪1,张晓东2,李贤斌2
),罗成1,陈浩1,杨继彪1,张晓东2,李贤斌2
Effect of Copper Content and Sintering Temperature on Friction and Wear Properties of Powder-metallurgical Fe-Cu Based Composites
SHI Lei1,ZHAO Qi1(),LUO Cheng1,CHEN Hao1,YANG Jibiao1,ZHANG Xiaodong2,LI Xianbin2
),LUO Cheng1,CHEN Hao1,YANG Jibiao1,ZHANG Xiaodong2,LI Xianbin2
图11. 铜含量为40%的铁-铜基材料在1196℃烧结1 h前后的XRD谱
Fig.11. XRD of Fe-Cu material with 40% copper content before and after sintering at 1196℃ for 1 h (a) before sintering; (b) after sintering