残余碳对取向硅钢初次和二次再结晶的影响
付勇军,雷家柳(
),廖庆玲,赵栋楠,张玉成
),廖庆玲,赵栋楠,张玉成
Effect of Residual Carbon on Primary and Secondary Recrystallization of Grain-oriented Silicon Steel
FU Yongjun,LEI Jialiu(),LIAO Qingling,ZHAO Dongnan,ZHANG Yucheng
),LIAO Qingling,ZHAO Dongnan,ZHANG Yucheng
图10. 不同残余碳含量取向硅钢脱碳退火样品的EBSD取向成像图
Fig.10. EBSD oriented images of samples after decarburization annealing for grain oriented silicon steel with different residual carbon content (a) Mapping image of sample with 0.0029% carbon; (b) Mapping image of sample with 0.0152% carbon; (c) Mapping image of sample with 0.0265% carbon; (d) ODF section diagram (φ2=45°) of sample with 0.0029% carbon; (e) ODF section diagram (φ2=45°) of sample with 0.0152% carbon; (f) ODF section diagram (φ2=45°) of sample with 0.0265% carbon; (g) Texture type on ODF section diagram (φ2=45°)