残余碳对取向硅钢初次和二次再结晶的影响
付勇军,雷家柳(
),廖庆玲,赵栋楠,张玉成
),廖庆玲,赵栋楠,张玉成
Effect of Residual Carbon on Primary and Secondary Recrystallization of Grain-oriented Silicon Steel
FU Yongjun,LEI Jialiu(),LIAO Qingling,ZHAO Dongnan,ZHANG Yucheng
),LIAO Qingling,ZHAO Dongnan,ZHANG Yucheng
图6. 不同残余碳含量取向硅钢高温退火样品的金相组织
Fig.6. Macrostructure of samples with different residual carbon content after high temperature annealing for grain oriented silicon steel (a) C=0.0029%; (b) C=0.0088%; (c) C=0.0152%; (d) C=0.0200%; (e) C=0.0265%