Effect of Residual Carbon on Primary and Secondary Recrystallization of Grain-oriented Silicon Steel
FU Yongjun,LEI Jialiu(),LIAO Qingling,ZHAO Dongnan,ZHANG Yucheng
),LIAO Qingling,ZHAO Dongnan,ZHANG Yucheng
图4. 不同残余碳含量取向硅钢脱碳退火样品的金相组织
Fig.4. Microstructure of samples with different residual carbon content after decarburization annealing for grain oriented silicon steel (a) C=0.0029%; (b) C=0.0088%; (c) C=0.0152%; (d) C=0.0200%; (e) C=0.0265%