钛增强Cu40Zn黄铜合金的粉末冶金制备及其力学性能
马晨,张鑫,潘登,郑飞洋,李树丰()
Fabrication and Mechanical Properties of Ti-Reinforced Cu40Zn Brass Alloy via Powder Metallurgy
MA Chen,ZHANG Xin,PAN Deng,ZHENG Feiyang,LI Shufeng()

图7. Cu40Zn-1.9Ti 试样的TEM照片、TEM明场像、选区电子衍射花样、HR1, HR2区域对应的高分辨照片和晶格衍射条纹

Fig.7. TEM micrographs of Cu40Zn-1.9Ti (a, b) bright field image; (c) selected area electron diffraction pattern corresponding to diff.1 remarked in Fig.7b; (d, e) high resolution TEM images corresponding to area HR1 and HR2 in Fig.7b; (f) diffraction fringe corresponding to area A3 in Fig.7b