Massive Preparation and Supercapacitor Performance of Layered Ti3C2
YANG Zhanxin, WU Qiong(), REN Yiqiao, QU Kaikai, ZHANG Zhehao, ZHONG Weili, FAN Guangning, QI Guochao
), REN Yiqiao, QU Kaikai, ZHANG Zhehao, ZHONG Weili, FAN Guangning, QI Guochao
图2. 烧结温度不同保温30 min的3Ti/1.2Al/1.9C样品的X射线衍射图谱、在1400℃保温30 min的3Ti/1.2Al/1.9C样品的X射线衍射图谱、烧结温度不同的3Ti/1.2Al/1.9C样品中Ti3AlC2的质量百分数以及刻蚀不同时间的Ti3C2的X射线衍射图谱
Fig.2. (a) X-ray diffraction patterns of 3Ti/1.2Al/1.9C samples obtained by sintering at different temperatures for 30 min; (b) X-ray diffraction patterns of 3Ti/1.2Al/1.9C sample obtained by sintering at 1400℃ for 30 min; (c) Mass percentage curve of Ti3AlC2 in 3Ti/1.2Al/1.9C obtained by sintering at different temperatures; (d) X-ray diffraction patterns of the precursor Ti3C2 obtained by different etching time