MgCl2对锌在干湿交替环境中腐蚀行为的影响
尹奇1,2,刘淼然1,3,刘雨薇1,潘晨1(
),王振尧1()
),王振尧1()
Effect of MgCl2 Deposite on Simulated Atmospheric Corrosion of Zn via Wet-dry Altertnating Corrosion Test
YIN Qi1,2,LIU Miaoran1,3,LIU Yuwei1,PAN Chen1(),WANG Zhenyao1()
),WANG Zhenyao1()
图6. 锌的2价腐蚀产物在浓度为4 mol·L-1的Cl-离子溶液中腐蚀产物的优势区
Fig.6. Predominant diagram of the divalent zinc compounds in 4 mol·L-1 Cl- solution at 25℃ and 1.013×105 Pa with 350×10-6 CO2， the calculation was based on the equilibrium constant listed in Table 3 and the ionic strength was set as 0