超高强度马氏体时效钢的力学行为与微观组织演化的关系
冯家伟1,2,牛梦超1,2,王威1(
),单以银1,杨柯1
),单以银1,杨柯1
Relationship Between Mechanical Behavior and Microstructure for an Ultra-high Strength Maraging Steel
FENG Jiawei1,2,NIU Mengchao1,2,WANG Wei1(),SHAN Yiyin1,YANG Ke1
),SHAN Yiyin1,YANG Ke1
图10. 2.4 GPa级马氏体时效钢在480℃时效过程中析出相的演变规律示意图
Fig.10. Schematic of evolution of precipitations in 2.4 GPa grade maraging steel during aging at 480℃