超高强度马氏体时效钢的力学行为与微观组织演化的关系
冯家伟1,2,牛梦超1,2,王威1(
),单以银1,杨柯1
),单以银1,杨柯1
Relationship Between Mechanical Behavior and Microstructure for an Ultra-high Strength Maraging Steel
FENG Jiawei1,2,NIU Mengchao1,2,WANG Wei1(),SHAN Yiyin1,YANG Ke1
),SHAN Yiyin1,YANG Ke1
图5. 图4e中选区(6 nm×6 nm×18 nm)的溶质原子分布和一维浓度分布
Fig.5. 3-D atoms mapping (a) in Fig.4e and corresponding 1-D concentration profile (b) of the selected region (6 nm×6 nm×18 nm)