Corrosion Behavior of Zinc Exposed to Salt Lake Area for 48 Months
Dan ZHANG,Zhenyao WANG
表1
图5中腐蚀产物层不同位置处元素的EDS分析结果
Table 1
EDS results of elements at different positions shown in Fig.5
Position No.
Mole fraction/%
C
O
Mg
Na
S
Al
Si
Cl
K
Ca
Zn
1
14.7
9.7
2.4
0
3.9
0
0
6.7
0.9
0.9
60.8
2
0
36.1
0
6.5
0
15.9
36.8
0
0
4.7
0
3
7.3
11.3
1.4
0
3.7
0
0
4.2
0
0
72.1
4
6.9
14.6
3.3
0
0
1.1
5.3
9.8
0.7
0
58.3
5
0
21.6
5.4
0
0
0.6
1.8
14
1.3
0
55.3