Ta含量对高性能镍基粉末高温合金高温拉伸性能的影响
王志成,王浩(
),黄海亮,胡本芙
),黄海亮,胡本芙
Effect of Ta on High Temperature Tensile Properties of Advanced Ni-based Powder Metallurgy Superalloys
Zhicheng WANG,Hao WANG(),Hailiang HUANG,Benfu Hu
),Hailiang HUANG,Benfu Hu
图5. 不同Ta含量合金在815℃拉伸后的断口形貌
Fig.5. Fracture morphology of different Ta content alloys after test at 815℃ (a) 0%Ta; (b) 1.2%Ta; (c) 2.4%Ta; (d) 3.6%Ta; (e) 4.8%Ta