原位微米/纳米TiC颗粒弥散强化304不锈钢的高温蠕变特性
倪自飞1,2(
),薛烽1
),薛烽1
High Temperature Creep Characteristics of In-Situ Micro-/Nano-meter TiC Dispersion Strengthened 304 Stainless Steel
Zifei NI1,2(),Feng XUE1
),Feng XUE1
图4. 在700℃/100 MPa条件下三种钢蠕变后的显微组织
Fig.4. Optical micrographs of the steels (a) 304SS; (b) 2TiC-304SS; (c) 5TiC-304SS after creep at 700℃/100 MPa