热压缩过程中2205双相不锈钢的组织演变和软化机制
吴天海1,王建军1(
),张影2,李花兵3,范光伟4,刘春明1
),张影2,李花兵3,范光伟4,刘春明1
Microstructural Evolution and Softening Mechanism of 2205 Duplex Stainless Steel during Hot Compression
Tianhai WU1,Jianjun WANG1(),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
图8. 不同变形量的钢中铁素体和奥氏体晶粒的百分比
Fig.8. Fraction of different types of grains in two phases for different hot compression strains (a) in ferrite; (b) in austenite