Microstructural Evolution and Softening Mechanism of 2205 Duplex Stainless Steel during Hot Compression
Tianhai WU1,Jianjun WANG1(),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
图6. 不同变形量试样的EBSD相组成图和相邻晶粒的取向差角的分布
Fig.6. EBSD phase map and distributions of adjacent grain misorientation angles of specimens with different hot compression strains (a, e) ε = 0.05, (b, f) ε = 0.3, (c, g) ε = 0.5, and (d, h) ε = 0.8, with a strain rate of 0.1 s-1 at 1050℃