Microstructural Evolution and Softening Mechanism of 2205 Duplex Stainless Steel during Hot Compression
Tianhai WU1,Jianjun WANG1(),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
图7. 真应变为0.8的钢两相中不同类型的显微结构
Fig.7. Different types of microstructures in two phases with a strain of 0.8 (a) recrystallized ferrite; (b) recovered austenite