热压缩过程中2205双相不锈钢的组织演变和软化机制
吴天海1,王建军1(
),张影2,李花兵3,范光伟4,刘春明1
),张影2,李花兵3,范光伟4,刘春明1
Microstructural Evolution and Softening Mechanism of 2205 Duplex Stainless Steel during Hot Compression
Tianhai WU1,Jianjun WANG1(),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
图5. 不同应变试样的光学显微组织
Fig.5. Optical microstructure of specimens of specimens with different hot compression strains (a) ε=0.05, (b) ε=0.3, (c) ε=0.5, and (d) ε=0.8, with a strain rate of 0.1 s-1 at 1050℃