热压缩过程中2205双相不锈钢的组织演变和软化机制
吴天海1,王建军1(
),张影2,李花兵3,范光伟4,刘春明1
),张影2,李花兵3,范光伟4,刘春明1
Microstructural Evolution and Softening Mechanism of 2205 Duplex Stainless Steel during Hot Compression
Tianhai WU1,Jianjun WANG1(),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
),Ying ZHANG2,Huabing LI3,Guangwei FAN4,Chunming LIU1
图2. 在不同变形条件下真应变为0.8试样的光学显微组织
Fig.2. Optical microstructure of specimens under different hot compression conditions with a strain of 0.8 (a) 850℃, (b) 1050℃, (c) 1250℃ at the strain rate of 0.1 s-1; (d) 850℃, (e) 1050℃, (f) 1250℃ at the strain rate of 1 s-1; (g) 850℃, (h) 1050℃, (i) 1250℃ at the strain rate of 10 s-1