锻态TB6钛合金β相区压缩变形行为和动态再结晶
欧阳德来,崔霞(
),鲁世强,徐勇
),鲁世强,徐勇
Hot Compressive Deformation and Dynamic Recrystallization of As-Forged Ti-Alloy TB6 During β Process
Delai OUYANG,Xia CUI(),Shiqiang LU,Yong XU
),Shiqiang LU,Yong XU
图3. 在变形温度为825℃、应变速率为0.01 s-1条件下不同应变的金相组织
Fig.3. Optical microstructures of specimens hot compressed at 825℃, strain rate of 0.01 s-1 and strain of ε=0 (a), ε=0.11 (b), ε=0.92 (c) and ε=1.61 (d)