终轧温度对Ti-V-Mo复合微合金钢组织演变和硬度的影响
张可1(
),赵时雨1,隋凤利1,李昭东2,叶晓瑜3,孙新军2,黄贞益1,雍岐龙2
),赵时雨1,隋凤利1,李昭东2,叶晓瑜3,孙新军2,黄贞益1,雍岐龙2
Effect of Finish Rolling Temperature on Microstructure Evolution and Hardness of Ti-V-Mo Complex Microalloyed Steel
Ke ZHANG1(),Shiyu ZHAO1,Fengli SUI1,Zhaodong LI2,Xiaoyu YE3,Xinjun SUN2,Zhenyi HUANG1,Qilong YONG2
),Shiyu ZHAO1,Fengli SUI1,Zhaodong LI2,Xiaoyu YE3,Xinjun SUN2,Zhenyi HUANG1,Qilong YONG2
图6. 不同终轧温度试样的TEM像
Fig.6. TEM images of samples finish rolled at different temperatures (a) 800℃, (b) 900℃, (c) 1000℃, (d) EDS of a particle in Fig. 6a