Kinetics of Dynamic Recrystallization of TB6 Ti-Alloy During Hot Compressive Deformation atTemperatures of β-phase Range
Delai OUYANG1,Shiqiang LU1,Xia CUI1(),Yong XU1,Haiming DU2,Huian ZHU1
),Yong XU1,Haiming DU2,Huian ZHU1
图3. 锻态TB6钛合金在不同热变形条件下的金相组织(ε=1.61)
Fig.3. Optical micrographs of specimens hot compressed with strain of 1.61: (a) 825℃,0.001 s-1; (b) 825℃, 0.01 s-1; (c) 825℃,0.1 s-1; (d) 825℃, 1 s-1; (e) 950℃, 0.001 s-1; (f) 1100℃, 0.001 s-1