偏离<001>取向15o的三种镍基单晶高温合金试样的中温蠕变变形行为
李钢1,张思倩2,张宗鹏2,王迪3,王栋3(
),董加胜3
),董加胜3
Creep Deformation of Three Samples Misaligned 15o from <001> Crystallographic Axis for a Nickel-based Single Crystal Superalloy DD413
Gang LI1,Siqian ZHANG2,Zongpeng ZHANG2,Di WANG3,Dong WANG3(),Jiasheng DONG3
),Jiasheng DONG3
图6. 不同滑移系对应的靠近<001>晶体取向偏转图
Fig.6. Directions of rotations in standard stereographic triangles for single crystals under (a) {111}<110> slip, the single crystals rotate toward <001>-<111>；(b) {111}<112>slip, the single crystals rotate toward <001>-<101>