偏离<001>取向15o的三种镍基单晶高温合金试样的中温蠕变变形行为
李钢1,张思倩2,张宗鹏2,王迪3,王栋3(
),董加胜3
),董加胜3
Creep Deformation of Three Samples Misaligned 15o from <001> Crystallographic Axis for a Nickel-based Single Crystal Superalloy DD413
Gang LI1,Siqian ZHANG2,Zongpeng ZHANG2,Di WANG3,Dong WANG3(),Jiasheng DONG3
),Jiasheng DONG3
图2. 偏离<001>取向15o的DD413合金在760℃/793 MPa条件下的应变-时间曲线
Fig.2. Strain-time curves of the DD413 alloy misaligned 15o from <001> at 760℃/793 MPa