同素异构转变对退火态Fe-15Mn-10Al-0.3C双相钢塑性的影响
刘营凯1,2,王白冰1,2,刘仁东3,郭金宇3,史文1,2(
)
)
Effect of Allotropic Transformation on Plasticity of Fe-15Mn-10Al-0.3C Dual Phase Steel during Annealing
LIU Yingkai1,2,WANG Baibing1,2,LIU Rendong3,GUO Jinyu3,SHI Wen1,2()
)
图12. 退火试样中α相与γ相之间偏离K-S关系图以及两相滑移系平行关系的占比变化趋势
Fig.12. Degree of deviation from K-S between γ and α in annealed samples (a) and (b) are the Schematic diagram of angular distribution deviating from K-S relationship of 1 s for SCRS and 2 min for DCRS; (c) and (d) are the proportion diagrams of different ferrite slip system parallel to austenite slip system during different annealing time after SCRS and DCRS respectively; (e) and (f) are the proportion diagrams of all ferrite slip system parallel to austenite slip system during different annealing time after SCRS and DCRS