时效温度对00Cr12Ni10MoTi马氏体时效不锈钢组织与性能的影响
张洪林1,2,马东平4,刘入杰1,3,王太江4,徐斌1,孙明月1(
),李殿中1,李依依1,于辉3
),李殿中1,李依依1,于辉3
Effect of Aging Temperature on Microstructure and Properties of 00Cr12Ni10MoTi Maraging Stainless Steel
ZHANG Honglin1,2,MA Dongping4,LIU Rujie1,3,WANG Taijiang4,XU Bin1,SUN Mingyue1(),LI Dianzhong1,LI Yiyi1,YU Hui3
),LI Dianzhong1,LI Yiyi1,YU Hui3
图6. 不同状态实验钢的TEM照片
Fig.6. TEM images of the tested steel under different condition (a) bright-field image of solid solution state; (b) bright-field image of aging state at 500℃; (c) bright-field image of precipitates in aging state at 500℃; (d) dark-field (DF) image of precipitates in aging state at 500℃; (e) [011]M selected area diffraction (SAD) pattern of matrix in aging state at 500℃; (f) schematics of SAD pattern with [011]M