时效温度对00Cr12Ni10MoTi马氏体时效不锈钢组织与性能的影响
张洪林1,2,马东平4,刘入杰1,3,王太江4,徐斌1,孙明月1(
),李殿中1,李依依1,于辉3
),李殿中1,李依依1,于辉3
Effect of Aging Temperature on Microstructure and Properties of 00Cr12Ni10MoTi Maraging Stainless Steel
ZHANG Honglin1,2,MA Dongping4,LIU Rujie1,3,WANG Taijiang4,XU Bin1,SUN Mingyue1(),LI Dianzhong1,LI Yiyi1,YU Hui3
),LI Dianzhong1,LI Yiyi1,YU Hui3
图4. 00Cr12Ni10MoTi钢试样的微观组织
Fig.4. Microstructure of 00Cr12Ni10MoTi samples (a) OM image of solid solution state sample; (b) SEM image of solid solution state sample; (c) OM image of aging state sample at 500℃; (d) SEM image of aging state sample at 500℃