Ti750合金中初生α相的体积分数对固溶温度的敏感性

陈朝阳,陈志勇,朱绍祥,刘建荣,王清江

Solution Temperature Sensitivity for Primary α-Phase Volume Fraction of Ti750 Alloys

Chaoyang CHEN,Zhiyong CHEN,Shaoxiang ZHU,Jianrong LIU,Qingjiang WANG

表1 αp相中Al元素含量(质量分数)

Table 1 Al content in αp phase of Ti750 alloy (mass fraction)

Alloys αp/% 1 2 3 4 5 Average Ti750-1 20 6.021 6.132 6.182 6.215 6.35 6.18 40 5.461 5.746 5.831 5.859 5.878 5.755 60 5.289 5.324 5.407 5.714 5.835 5.514 Ti750-2 20 6.117 6.182 6.216 6.249 6.303 6.213 40 6.048 6.107 6.196 6.228 6.299 6.175 60 6.009 6.024 6.04 6.146 6.248 6.09