Ti750合金中初生α相的体积分数对固溶温度的敏感性
陈朝阳1,2,陈志勇1,朱绍祥1,刘建荣1(
),王清江1
),王清江1
Solution Temperature Sensitivity for Primary α-Phase Volume Fraction of Ti750 Alloys
CHEN Chaoyang1,2,CHEN Zhiyong1,ZHU Shaoxiang1,LIU Jianrong1(),WANG Qingjiang1
),WANG Qingjiang1
图7. 在930℃热处理时αp相的体积分数随保温时间(τ)的变化
Fig.7. Relationship between the volume fraction of αp phase and solution time of Ti750 alloy at 930℃