Ti750合金中初生α相的体积分数对固溶温度的敏感性
陈朝阳1,2,陈志勇1,朱绍祥1,刘建荣1(
),王清江1
),王清江1
Solution Temperature Sensitivity for Primary α-Phase Volume Fraction of Ti750 Alloys
CHEN Chaoyang1,2,CHEN Zhiyong1,ZHU Shaoxiang1,LIU Jianrong1(),WANG Qingjiang1
),WANG Qingjiang1
图2. 在不同温度固溶热处理后Ti750合金的显微组织
Fig.2. Microstructure of alloy after solution treatment at various temperature for Ti750-1 with 0.25% Mo at 940℃ (a), 980℃ (b) and 1000℃ (c) and for Ti750-2 with 1.0% Mo at 940℃ (d), 980℃ (e) and 1000℃ (f)