预变形程度和变形温度对CoCrFeMnNi高熵合金的变形机制及后续再结晶行为的影响

涂坚,刘雷,丁石润,李建波,周志明,董安平,黄灿

Effect of Degree and Temperature of Pre-deformation on Deformation Mechanism and Subsequent Recrystallization Behavior of High-entropy Alloy CoCrFeMnNi

Jian TU,Lei LIU,Shirun DING,Jianbo LI,Zhiming ZHOU,Anping DONG,Can HUANG

图4 室温轧制态的样品(中等应变量30%)在不同温度再结晶热处理后的EBSD图

Fig.4 EBSD maps of deformed samples at room temperation with 30% deformation degree under different annealing temperature, including RA-30%-400℃, RA-30%-700℃ and RA-30%-1000℃ samples