Ni-Cr-Co-Mo-W-Ta-Al合金在900℃和1000℃的高温氧化行为*

卢旭东, 王复利

Isothermal Oxidation Behaviour of Ni-Cr-Co-Mo-W-Ta-Al Superalloy at 900℃ and 1000℃

LU Xudong, WANG Fuli

表1 相关化合物的吉布斯自由能

Table 1 Gibbs free energy for the formation of related compounds (kJmol-1)

Compound 900℃ 1000℃ Al2O3 -1296 -1263 Cr2O3 -814 -789 NiO -134 -126 CoO -153 -145 Ta2O5 -1541 -1500 AlN -189 -177 CrN -27 -20 TaN -152 -144