元素V对镍基柱状晶合金显微组织和高温蠕变性能的影响

于兴福, 周金华, 吴玉超, 杨月, 王宇飞, 满延林, 黄爱华

Effect of V on Microstructure and High Temperature Creep Properties of Diretional Solidified Nickel-base Superalloys

YU Xingfu, ZHOU Jinhua, WU Yuchao, YANG Yue, WANG Yufei, MAN Yanlin, HUANG Aihua

表1 定向凝固合金棒的主要化学成分

Table 1 Nominal composition of bars (%, mass fraction)

C Cr Al Mo Ti Co V B Ni Alloy 1 0.147 9.03 5.22 3.05 4.67 10.23 0.62 0.015 Bal. Alloy 2 0.145 9.01 5.26 3.04 4.67 10.24 0.96 0.016 Bal. Alloy 3 0.146 9.00 5.28 3.06 4.65 10.23 1.04 0.015 Bal.