w(MgO)对高钛高炉渣黏流特性的影响*
|
|
唐昭辉, 丁学勇, 董越, 刘程宏, 魏国
|
Influence of w(MgO) on Viscous Flow Property of High Ti-containing Blast Furnace Slag
|
|
TANG Zhaohui, DING Xueyong, DONG Yue, LIU Chenghong, WEI Guo
|
|
| 表2 炉渣试样成分组成/% |
| Table 2 Experimental compositions (%) |
|
| R2 | w(CaO) | w(SiO2) | w(MgO) | w(A12O3) | w(TiO2) | w(Ti(C,N)) | w* | Slag proportion | | 1.00 | 27.52% | 27.52% | 8.00% | 14.00% | 20.00% | 0.28% | 2.68% | 83.42% | | 1.00 | 26.27% | 26.27% | 10.00% | 14.00% | 20.00% | 0.32% | 3.14% | 97.63% | | 1.00 | 25.33% | 25.33% | 12.00% | 14.00% | 20.00% | 0.31% | 3.03% | 94.14% | | 1.10 | 28.83% | 26.21% | 8.00% | 14.00% | 20.00% | 0.28% | 2.68% | 83.42% | | 1.10 | 27.56% | 25.05% | 10.00% | 14.00% | 20.00% | 0.32% | 3.07% | 95.90% | | 1.10 | 26.56% | 24.14% | 12.00% | 14.00% | 20.00% | 0.31% | 2.99% | 92.43% | | 1.20 | 30.02% | 25.02% | 8.00% | 14.00% | 20.00% | 0.28% | 2.68% | 83.42% | | 1.20 | 28.77% | 23.98% | 10.00% | 14.00% | 20.00% | 0.30% | 2.95% | 91.80% | | 1.20 | 27.75% | 23.12% | 12.00% | 14.00% | 20.00% | 0.29% | 2.84% | 88.52% |
|
|
|